Place of Origin : Jiangsu, China (Mainland)
Brand Name : Chen's Liner
Certification : ISO 9001:2008
Model Number : DF145
MOQ : 5 Ton/Tons
Price : Discuss in email
Packaging Details : Packed by steel pallets.
Delivery Time : It depends on the quantity to be ordered.
Payment Terms : L/C,T/T
Supply Ability : 30000 Ton/Tons per Year
Port : Shanghai
Material : Cr15
Hardness : ≥HRC60
Impact Value : As per drawings
Assembly Face : More than5J
Application : Jaw Crushers
Product Name : Crusher Wear Parts
Crusher Wear Parts Free Surface High Cr Jaw Plates For High Toughness Values
Quick Details
1. The series are designed for high abrasion performance and high toughness values.
2. Hardness:more than HRC60.
3.Microstructure:Fine Martensite + Carbide + retained Austenite(≤6%).
High Cr Jaw Plates for Jaw Crushers
1. Hardness difference from surface to center is less than HRC2.
2. The Cr15 Jaw Plates are designed for high abrasion performance.
3. Hardness:more than HRC60.
4. Surface of castings is free from burnt sand & smooth.
5. It is free from hard spot,visible injurious defects such as blow hole,porosity,shrinkage,cracks,cold-shuts.
6. Excellent wear performance:under same working condition,the wear property of High Chrome Jaw Plates is four times of that of high manganese steel plates and twice of that of low Chrome alloy steel plates.
In the recent 20 years,our liners have been widely used in large,medium and small ball mills in Chinese power generation,mining,cement,Chemical engineering and metallurgical industries and super fine pulverizing equipments.It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co.,Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |
- |
3.3~10 |
Re |
≤0.02 |
≤0.02 |
≤0.02 |
- |
- |
- |
- |
Equivalent Specifications |
DL/T 681-1999
GB/T26651-2011 |
AS 2074 L2B Mod |
DL/T 681-1999 |
GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401. |
GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12 |
GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A |
|
Material Type |
Martensite Steel |
Martensite or Pearlitic Cr Mo Steel |
Martensite Steel |
Martensite matrix |
Austenitic Mn Steel |
- |
|
Hardness |
HRc≥48 |
HB470 & HB 321~370 |
HRc≥50 |
HRc≥56 |
HB≤300 |
HRc≥56 |
|
Impact Value |
Ak≥40J |
- |
Ak≥10J |
Ak≥4J |
Ak≥80J |
- |
Our foundry has complete melting,heat treatment and test equipments,such as mid-frequency induction electrical furnaces,quenching and tempering furnaces,blast shot,spectrometer,Rockwell and Brinell Hardness tester,impactor,UT tester and metallographic microscope.We achieved the certificate of quality management system ISO 9001:2008.We have been exporting castings to oversea markets,such as Brazil, Australia and South Africa.
![]() |
Crusher Wear Parts Free Surface High Cr Jaw Plates For High Toughness Values Images |